電解銅(Cu) 磷銅合金 鉛錠(Pb) 錫錠(Zn)
鋅錠(Zn) 鋁錠(Al) 電解錳(Mn) 電解鎳(Ni)
| 美國有色金屬合金元素含量表（我司常用牌號） 參考標準：ASTM/B224-1998 | |||||||||||
| 銅合金(%) | |||||||||||
| 牌號 | Cu | Sn | Pb | Zn | Al | Fe | Mn | Ni+Co | P | Sb | 國內相似 |
| C83400 | 88-92 | ≤0.2 | ≤0.5 | 8-12 | ≤0.005 | ≤0.25 | / | ≤1.0 | / | ≤0.25 | H90 |
| C83600 | 84-86 | 4-6 | 4-6 | 4-6 | ≤0.005 | ≤0.3 | / | ≤1.0 | / | ≤0.25 | ZQSn5-5-5 |
| C84400 | 78-82 | 2.3-3.5 | 6-8 | 7-10 | ≤0.005 | ≤0.4 | / | ≤1.0 | ≤0.02 | ≤0.25 | ZQSn6-6-3 |
| C85500 | 59-63 | ≤0.2 | ≤0.2 | 余量 | / | ≤0.2 | ≤0.2 | ≤0.2 | / | / | H62 |
| C85700 | 58-64 | 0.5-1.5 | 0.8-1.5 | 32-40 | ≤0.8 | ≤0.7 | / | ≤1.0 | / | / | ZH59-1 |
| C86300 | 60-66 | ≤0.2 | ≤0.2 | 22-28 | 5.0-7.5 | 2-4 | 2.5-5 | ≤1.0 | / | / | ZCu25-6-3-3 |
| C90500 | 86-89 | 9-11 | ≤0.5 | 1-3 | ≤0.005 | ≤0.2 | / | ≤1.0 | ≤0.05 | ≤0.2 | ZQSn10-2 |
| C90710 | 余量 | 10-12 | ≤0.25 | ≤0.05 | ≤0.005 | ≤0.1 | / | ≤0.1 | 0.05-1.2 | ≤0.2 | ZQSn10-1 |
| C93200 | 81-85 | 6.3-7.5 | 6-8 | 1-4 | / | ≤0.2 | / | ≤1.0 | ≤0.15 | ≤0.35 | ZQSn6-6-3 |
| C93700 | 83.0min | 9-11 | 8-11 | ≤0.8 | / | / | / | ≤0.5 | ≤0.08 | ≤0.5 | ZQPbD10-10 |
| C93800 | 75-79 | 6.3-7.5 | 13-16 | ≤0.8 | / | ≤0.15 | / | ≤1.0 | ≤1.5 | ≤0.8 | ZQPbD15-7 |
| C94100 | 72-79 | 4.5-6.5 | 18-22 | ≤1.0 | / | ≤0.25 | / | ≤1.0 | ≤0.05 | ≤0.8 | ZQPbD20-5 |
| C95200 | ＞86 | / | / | / | 8.5-9.5 | 2.5-4 | / | / | / | / | ZQAl9-3 |
| C95400 | ＞83 | / | / | / | 10-11.5 | 3-5 | ≤0.5 | ≤1.5 | / | / | ZQAl10-3 |
| 國內有色金屬合金元素含量表 參考標準：GB/T 1173-1995 | |||||||||||
| 銅合金(%) | |||||||||||
| 種類(lèi) | 牌號 | Cu | Sn | Pb | Zn | Al | Fe | Mn | Ni | P | 雜質(zhì)總和 |
| 高 鉛 錫 青 銅 | ZQPbD10-10 | 余量 | 9-11 | 8-11 | ≤2.0 | ≤0.01 | ≤0.25 | ≤0.2 | ≤2.0 | ≤0.05 | ≤1.0 |
| ZQPbD15-8 | 余量 | 7-9 | 13-17 | ≤2.0 | ≤0.01 | ≤0.25 | ≤0.2 | ≤2.0 | ≤0.1 | ≤1.0 | |
| ZQPbD15-7 | 余量 | 6.5-9 | 13-17 | ≤2.0 | ≤0.15 | ≤0.15 | ≤0.2 | ≤2.0 | ≤0.05 | ≤1.0 | |
| ZQPbD20-5 | 余量 | 4-6 | 18-23 | ≤2.0 | ≤0.01 | ≤0.25 | ≤0.2 | ≤2.5 | ≤1.5 | ≤1.0 | |
| ZQPbD17-4-4 | 余量 | 3.5-5 | 14-20 | 2-6 | ≤0.05 | ≤0.4 | / | / | ≤0.05 | ≤0.75 | |
| 錫 青 銅 | ZQSn10-1 | 余量 | 9-11.5 | ≤0.25 | ≤0.05 | ≤0.01 | ≤0.1 | ≤0.05 | ≤0.1 | 0.5-1 | ≤1.0 |
| ZQSn10-2 | 余量 | 9-11 | ≤0.25 | 1-3 | ≤0.01 | ≤0.1 | ≤0.05 | ≤0.1 | 0.5-1 | ≤1.0 | |
| ZQSn10-5 | 余量 | 9-11 | 4-6 | ≤0.05 | ≤0.01 | ≤0.1 | ≤0.05 | ≤0.1 | 0.5-1 | ≤1.0 | |
| ZQSn6-6-3 | 余量 | 5-7 | 2-4 | 5-7 | ≤0.01 | ≤0.3 | / | ≤2.5 | ≤0.05 | ≤1.0 | |
| ZQSn5-5-5 | 余量 | 4-6 | 4-6 | 4-6 | ≤0.01 | ≤0.3 | / | ≤2.5 | ≤0.05 | ≤1.0 | |
| 鋁 青 銅 | ZQAl9-3 | 余量 | ≤0.3 | ≤0.2 | ≤0.4 | 8.5-10 | 2-3 | ≤1.0 | ≤3.0 | / | ≤1.0 |
| ZQAL9-4 | 余量 | ≤0.3 | ≤0.2 | ≤0.4 | 8.5-10 | 2.5-4 | ≤1.0 | ≤3.0 | / | ≤1.0 | |
| ZQAL10-3 | 余量 | ≤0.3 | ≤0.2 | ≤0.4 | 8.5-11 | 2-4 | ≤1.0 | ≤3.0 | / | ≤1.0 | |
| ZQAL9-4-4-2 | 余量 | / | ≤0.02 | / | 8.5-10.0 | 4.0-5.0 | 0.8-2.5 | 4.0-5.0 | / | ≤1.0 | |
| 高力黃銅 | ZCuZn25Al6Fe3Mn3 | 60-66 | ≤0.2 | ≤0.2 | 23-28 | 4.5-7 | 2-4 | 1.5-4 | ≤3.0 | / | ≤2.0 |
| 錳 黃 銅 | ZHMn58-2 | 57-60 | / | ≤0.01 | 余量 | / | ≤1.0 | 1-2 | / | ≤0.1 | ≤1.2 |
| ZHMn57-3-1 | 55-58.5 | / | ≤0.2 | 余量 | 0.5-1.5 | ≤1.0 | 2.5-3.5 | / | ≤0.01 | ≤1/3 | |
| ZHMn55-3-1 | 53-58 | ≤0.2 | ≤0.5 | 余量 | ≤0.3 | ≤0.5-1.5 | 3-4 | / | ≤0.02 | ≤1.5 | |
| 鉛 黃 銅 | ZHPb63-3 | 62-64 | / | 2.4-3.0 | 余量 | ≤0.5 | ≤0.1 | / | / | ≤0.01 | ≤o.75 |
| ZHPb63-0.1 | 61.5-53.5 | / | 0.05-0.3 | 余量 | ≤0.2 | ≤0.15 | / | / | ≤0.01 | ≤0.75 | |
| ZHPb59-3 | 57.5-59.5 | / | 2-3 | 余量 | / | ≤0.5 | / | ≤0.5 | / | ≤1.2 | |
| ZHPb59-1 | 57-60 | / | 0.8-1.9 | 余量 | / | ≤0.5 | / | ≤1.0 | / | ≤1.0 | |
| 普 通 黃 銅 | H68 | 67-70 | / | ≤0.03 | 余量 | / | ≤0.1 | / | ≤0.5 | / | ≤1.0 |
| H65 | 63.5-68.0 | / | ≤0.03 | 余量 | / | / | / | / | ≤0.01 | ≤1.0 | |
| H62 | 60.5-63.5 | / | ≤0.08 | 余量 | / | ≤0.15 | / | ≤0.5 | / | ≤1.5 | |
| H59 | 57-60 | / | ≤0.5 | 余量 | / | ≤0.3 | / | / | ≤0.01 | ≤1.0 | |
| 鋁合金(%) | |||||||||||
| 牌號 | Al | Si | Mg | Cu | Mn | Zn | Ti+Zr | Be | Sn | Pb | |
| 6061 | 余量 | 0.4-0.8 | 0.8-1.2 | / | ≤0.15 | ≤0.25 | ≤0.15 | / | / | / | |
| 6063 | 余量 | 0.2-0.6 | 0.45-0.9 | ≤0.1 | ≤0.1 | ≤0.1 | ≤0.1 | / | / | / | |
| ZL101 | 余量 | 6.5-7.5 | 0.25-0.45 | ≤0.2 | ≤0.35 | ≤0.3 | ≤0.25 | ≤0.1 | ≤0.01 | ≤0.05 | |
| ZL102 | 余量 | 10.0-13.0 | ≤0.1 | ≤0.3 | ≤0.5 | ≤0.1 | ≤0.2 | / | / | / | |
| ZL104 | 余量 | 8.0-10.5 | 0.17-0.35 | ≤0.1 | 0.2-0.5 | ≤0.25 | ≤0.15 | / | ≤0.01 | ≤0.01 | |
| ZL105 | 余量 | 4.5-5.5 | 0.4-0.6 | 1.0-1.5 | ≤0.5 | ≤0.3 | ≤0.15 | ≤0.1 | ≤0.01 | ≤0.05 | |
| ZL106 | 余量 | 7.5-8.5 | 0.3-0.5 | 1.0-1.5 | 0.3-0.5 | ≤0.2 | 0.1-0.25 | / | ≤0.01 | ≤0.05 | |
| ZL107 | 余量 | 6.5-7.5 | ≤0.1 | 3.5-4.5 | ≤0.3 | ≤0.3 | / | / | ≤0.01 | ≤0.05 | |
| ZL108 | 余量 | 11.0-13.0 | 0.4-1.0 | 1.0-2.0 | 0.3-0.9 | ≤0.2 | ≤0.2 | / | ≤0.01 | ≤0.05 | |
| ZL110 | 余量 | 4.0-6.0 | 0.2-0.5 | 5.0-8.0 | ≤0.5 | ≤0.6 | / | / | ≤0.01 | ≤0.05 | |
| ZL116 | 余量 | 6.5-8.5 | 0.35-0.55 | ≤0.3 | ≤0.1 | ≤0.3 | ≤0.1 | 0.15-0.4 | ≤0.01 | ≤0.05 | |
| 鋅基合金(%) | |||||||||||
| 牌號 | Zn | Al | Cu | Mg | Fe | Pb | Sn | Mn | Cr | Ni | |
| ZA272 | 余量 | 25.0-28.0 | 2.0-2.5 | 0.01-0.02 | ≤0.075 | ≤0.006 | ≤0.003 | ≤0.01 | ≤0.01 | ≤0.01 | |
| ZA303 | 余量 | 28.0-32.0 | 2.5-4.0 | 0.01-0.02 | ≤0.075 | ≤0.006 | ≤0.003 | ≤0.01 | ≤0.01 | ≤0.01 | |